Click to view and choose plate sizes available
This plate is fabricated via resin infusion and deploys a T700 (or equivalent) carbon fiber. In addition to being stiffer than aluminum carbon fiber plate this thicker version can be machined quite easily and shaped to yield a very interesting aesthetic often seen in knife handles or other products. Other manufacturers have dubbed this plate or ones similar "Artisan". Both sides have a peel ply finish which is matte / textured by default and with a quick cleaning can be bond ready.
P/N | 416-0606 | 416-1212 | 416-1224 | 416-2424 | 416-2448 |
---|---|---|---|---|---|
Application | Tooling Plates / Support Structures | Tooling Plates / Support Structures | Tooling Plates / Support Structures | Tooling Plates / Support Structures | Tooling Plates / Support Structures |
Materials | Standard Modulus Carbon | Standard Modulus Carbon | Standard Modulus Carbon | Standard Modulus Carbon | Standard Modulus Carbon |
Pattern | 3k 2X2 Twill Weave | 3k 2X2 Twill Weave | 3k 2X2 Twill Weave | 3k 2X2 Twill Weave | 3k 2X2 Twill Weave |
Color | Black | Black | Black | Black | Black |
Finish | Matte / Matte | Matte / Matte | Matte / Matte | Matte / Matte | Matte / Matte |
Panel Thickness | 0.440000 | 0.440000 | 0.440000 | 0.440000 | 0.440000 |
Plate / Panel Size | 5.75" x 5.75" / 146.05mm x 146.05mm | 11.75" x 11.75" / 298.45mm x 298.45mm | 11.75" x 23.75" / 298.45mm x 603.25mm | 24" x 24" / 609.6mm x 609.6mm | 24" x 48" / 609.6mm x 1219.2mm |
Width | 5.75 | 12.0 | 12.0 | 24.0 | 24.0 |
Thickness | 0.44 | 0.44 | 0.44 | 0.44 | 0.44 |
Length | 5.75 | 12 | 24 | 24 | 48 |
Weight | 0.76 | 3.485 | 6.97 | 13.939 | 27.878 |
Length (max continuous) | 12.0 | 24.0 | 24.0 | 48.0 | |
Areal Density | 3.485 | 3.485 | 3.485 | 3.485 | |
Volumetric Density | 0.055 | 0.055 | 0.055 | 0.055 | |
Primary Fiber | Toray T700S | Toray T700S | Toray T700S | Toray T700S | |
Primary Resin / Hardener | Rhino 1411/4111 | Rhino 1411/4111 | Rhino 1411/4111 | Rhino 1411/4111 |
All laminate properties and mechanical calculations are based on Classical Lamination Theory and should be used as a reference only. Rock West Composites does not guarantee these properties or calculations.
P/N | 416-0606 | 416-1212 | 416-1224 | 416-2424 | 416-2448 |
---|---|---|---|---|---|
Avg EX Young's Modulus | 9300000.0 | 9300000.0 | 9300000.0 | 9300000.0 | |
Avg EY Young's Modulus | 9300000.0 | 9300000.0 | 9300000.0 | 9300000.0 | |
GXY Shear Modulus | 600000.0 | 600000.0 | 600000.0 | 600000.0 | |
X Tensile Yield Strength | 103000.0 | 103000.0 | 103000.0 | 103000.0 | |
X Compressive Yield Strength | 89000.0 | 89000.0 | 89000.0 | 89000.0 | |
Y Tensile Yield Strength | 103000.0 | 103000.0 | 103000.0 | 103000.0 | |
Y Compressive Yield Strength | 89000.0 | 89000.0 | 89000.0 | 89000.0 | |
XY Shear Strength | 10636.0 | 10636.0 | 10636.0 | 10636.0 | |
CTEX | 2.00E-06 | 2.00E-06 | 2.00E-06 | 2.00E-06 | |
CTEY | 2.00E-06 | 2.00E-06 | 2.00E-06 | 2.00E-06 | |
Poisson's Ratio vXY | 0.035 | 0.035 | 0.035 | 0.035 | |
Poisson's Ratio vYX | 0.035 | 0.035 | 0.035 | 0.035 |